Beryllium Copper 25 is a Copper base alloy with the capability of being strengthened by precipitation heat treatment. The alloy furnishes the best combination of electrical conductivity, corrosion resistance and mechanical strength necessary for numerous electronic and electromechanical devices. The alloy is quite satisfactory for fabrication with good formability and joining characteristics. Forming is readily accomplished from the annealed temper. Severe bending will be less successful from hard or heat treated tempers and requires large fold radius ratios. Beryllium Copper 25 is able to be soldered, brazed, and welded by most standard techniques. The brazing temperature must be kept under 1450º F and cycle time minimized to avoid loss of heat treated strength. Heat treating should be performed subsequent to welding to obtain uniform high strength. The alloy is not susceptible to an increase in magnetic attraction from plastic deformation during service

HPM® 965 is a high purity Nickel-Iron alloy that exhibits moderate electrical resistivity and a high temperature coefficient of resistance. This combination of electrical characteristics makes it suitable for use as a self-regulating heating element or temperature sensor, such as use in flexible metal foil heaters. The alloy can be readily formed in the annealed temper and can be joined by standard welding methods. Available Sizes: HPM® 965 is available from Hamilton Precision Metals as foil and strip product in thicknesses from 0.0005” to 0.015” (0.0127 mm to 0.38 mm) and in widths up to 12” (304.8 mm). It is also available as thin as 0.000100” (0.00254 mm) and in widths up to 4” (101.6 mm) maximum.