Base material for cold drawing is ASTM A276. UNS S32760 F55 solution annealed material that complies with Condition A. After cold drawing (strain hardening) material meets ASTM A276, UNS 32760 F55 Condition S. Material that meets required impact test requirements will be further designated as variant 'FG', 'FLT', or 'FLT+'

ASMS659 is a corrosion resistant steel. We hold this grade in round bar form in both the solution treated condition (Condition A) and in the H1025 precipitation treated (aged) condition. The material is typically used for part s requiring corrosion resistance and high strength up to 300oC. The material exhibits good ductility and strength in the transverse direction in large section sizes SIZES STOCKED: Condition A – 9.5 mm dia – 152.4 mm dia H1025 condition – 12.7 mm dia – 152.4 mm dia

13-8 Mo VIM-VAR steel is a precipitation hardening martensitic stainless steel/ It offers excellent strength, fracture toughness and transverse mechanical properties. The material is resistant to stress, corrosion cracking and has the high strength characteristics common to the family of precipitation hardening steels. The alloy is double vacuum remelted (VIM-VAR) which assures low gas content, improved homogeneity and superior cleanliness

Alloy 17-4 PH is a chromium-copper precipitation hardening martensitic stainless steel with Cu and Nb/Cb additions. 17-4PH Stainless Steel combines high strength, hardness (up to 572°F / 300°C), and moderate corrosion resistance. Alloy 17-4 PH withstands corrosive attacks better than any of the standard hardenable stainless steels and is comparable to Alloy 304 in most media. The alloy is subject to crevice or pitting attack if exposed to stagnant seawater for any length of time, although it is corrosion resistant in some chemical, petroleum, paper, dairy and food processing industries(equivalent to 304L grade). Mechanical properties can be improved (high strength and superior corrosion resistance) when precipitation hardened from Condition A to one of the Condition H tempers. We supply 17-4 PH in the H1150D condition. This is double aged at a temperature between 1140° F and 1160° F for 3.75 hours to 4.